World’s Largest Transmission Capacity with Standard Diameter Multi-Core Optical Fiber: Accelerate Multi-Core Fiber Application using Current Standard Technology (PDF: 590KB)

8 August, 2017 Nippon Telegraph and Telephone Corporation

KDDI Research, Inc. Sumitomo Electric Industries, Ltd.

Fujikura Ltd. Furukawa Electric Co., Ltd.

NEC Corporation Chiba Institute of Technology

World's Largest Transmission Capacity with Standard Diameter Multi-Core Optical Fiber: Accelerate Multi-Core Fiber Application using Current Standard Technology

Nippon Telegraph and Telephone Corporation (NTT, Chiyoda-ku, Tokyo, President and CEO: Hiroo Unoura), and six partners, KDDI Research, Inc. (KDDI Research, Fujimino, Saitama, President and CEO: Yasuyuki Nakajima), Sumitomo Electric Industries, Ltd. (Sumitomo Electric, Cyuo-ku, Osaka, President: Osamu Inoue), Fujikura Ltd. (Fujikura, Koto-ku, Tokyo, President and CEO Masahiko Ito), Furukawa Electric Co., Ltd. (Furukawa, Chiyoda-ku, Tokyo, President: Keiichi Kobayashi), NEC Corporation (NEC, Minato-ku, Tokyo, President and CEO: Takashi Niino), and Chiba Institute of Technology (CIT, Narashino, Chiba, President:

Kazuhito Komiya) have demonstrated the world's largest transmission capacity of 118.5 Tera-bit/s *1 using a

multi-core fiber with four optical paths (cores) in the same diameter of currently used optical fiber.

A conventional glass diameter (125 m)*2 in accordance with the international standard enables us to use existing optical fiber fabrication and optical connector technologies effectively. This achievement proves the concept of multi-core fiber based long-haul and large capacity transmission system consisting of multiple vendor technologies, and it makes significant progress on practical use of the multi-core fiber technology.

We will aim to introduce the standard diameter multi-core fiber by the early 2020s. We will also continue to contribute the realization of a future optical infrastructure which can support variety of data communication demands.

This remarkable achievement was reported in 4 August as a postdeadline paper*3 at the Opto Electronics and

Communications Conference (OECC 2017), the largest conference on optical communication in Asia Pacific-Rim, which was held at Sands Expo and Convention Centre, Singapore.

This work was partially based on work commissioned by the National Institute of Information and Communications Technology (NICT).

Figure 1 Features of the proposed multi-core fiber [Research Background]

World wide spread of various mobile terminal and data services continuously increases the transmission capacity more than 10% per year all over the world. This trend may cause capacity crunch in the currently used optical fiber by the late 2020s. Moreover, the expansion of optical fiber count and the convergence of optical wiring particularly in the data center and/or central office, which is caused by the world wide data capacity increase, would be serious problem.

With these as backgrounds, a multi-core fiber having multiple optical paths (cores) in one fiber has been investigated intensively all over the world in order to overcome the future capacity crunch and to realize the high density or space saving optical facilities. For example, ultra large capacity transmission experiments using a multi-core fiber with 10 cores or more have been demonstrated*4. However, these high core count multi-core fiber usually needs a thicker glass diameter, and it requires an extreme advance in the fabrication process and

further development on sub-components. As a result, it is considered that 10 years or so would be necessary to make the high core count multi-core fiber practical.

In order to accelerate using the multi-core fiber technology, NTT, KDDI Research, Sumitomo Electric, Fujikura, Furukawa, NEC, and CIT developed a multi-core fiber with a conventional diameter in accordance with the current International standard. It enables to use existing optical fiber technology even though it limits the number of cores to 4-5.

[Summary of Achievements]

NTT, KDDI Research, Sumitomo Electric, Fujikura, Furukawa, NEC, and CIT:

• Clarified the design guideline for a multi-core fiber with conventional glass diameter in accordance with International standard,

• Realized a multi-core transmission line composed of a standard diameter multi-core fibers fabricated by multiple vendors,

• Proved a beyond 100 Tera-bit/s transmission using the standard diameter multi-core fiber transmission line.

  These studies led to three major achievements:

• 4-5 cores can be arranged within a 125 m gla s s d ia me te r wh ile ma inta ining the s a me tra nsmis s ion

  quality with the current optical fiber,

• A 316 km long multi-core transmission line is realized with a 0.21 dB/km average loss*5 concatenating the standard diameter multi-core fibers (4 cores) fabricated by multiple vendors randomly,

• World's largest transmission capacity of 118.5 Tera-bit/s is achieved among a standard diameter optical fiber using a multi-core transmission system composed of the above multi-core transmission line, multi-core optical amplifiers, and the existing optical connectors.

As a results, we successfully revealed the capacity extensionability and affinity with the existing technology of our multi-core fiber in accordance with the International standard of the current optical fiber.

[Detail of Achievements]

1. Design Guideline

   During the fabrication process of an optical fiber, a relatively large size glass rod with a diameter of several to ten centimeters, namely preform, is prepared. An optical fiber is realized by melting and drawing the preform while keeping the geometrical similarity. When a glass diameter of an optical fiber is enlarged two times (e.g.

   from conventional 125 m to 250 m), the fabrication length obtained with the same size preform is reduced to a quarter. Therefore, the increase in the glass diameter directly affects the mass-productivity of an optical fiber. The current optical communication system is commonly using a single-mode fiber (SMF) with a core diameter

   of about 10 m and it which can be used in all the telecommunication wavelength region (1260 nm - 1625 nm).

   We then aim to realize a multi-core fiber with two features: i) having a glass and coating diameter of 1250.7

   m and 235-265 m in accordance with the International standard of the current optical fiber, ii) whose individual core can have the similar transmission quality with the commonly used SMF. In a multi-core fiber, the optical signal interference between neighboring cores*6 should be reduced sufficiently. NTT and KDDI Research revealed that 4-5 cores can be arranged in a 125 m glass diameter.

   • Assuming an optical fiber preform capable to fabricate a 100 km long optical fiber with a 125 m glass diameter, the fabrication length is reduced to be quarter when a glass diameter is enlarged two times.

   • 4-5 cores can be arranged in a standard glass diameter while keeping the similar transmission quality with commonly used SMF.

   Figure 2 Schematic image of productivity reduction caused by a glass diameter enlargement, and example multi-core fibers with a standard glass diameter
2. Multi-core transmission line composed of multiple vendor optical fibers

   Based on the above design guideline, Sumitomo Electric, Fujikura, and Furukawa individually fabricated a multi-core fibers with four cores and more than 100 km length. All multi-core fibers can be used in the 1260 nm

   - 1625 nm wavelength region, and having the similar transmission property to the current SMF (cf. Mode filed

   diameter (MFD)*7 at 1550 nm is 9-10 m).

   The fabricated multi-core fibers were divided into a 20-40 km long pieces, and three transmission spans with a length of 104-107 km were re-constructed by splicing the multi-core fibers provided by different vendors intentionally. A satisfactory low loss features which is comparable to the conventional SMF was achieved. An average loss of four cores in each span was 0.22 dB/km or less including splicing losses. We spliced two multi-core fibers by melting each end, namely fusion splice technology. A 0.21 dB/km loss property was achieved as the average of all three spans.

   These achievements indicate that our standard diameter multi-core fiber with similar transmission quality (MFD) with the conventional SMF enables us to greatly improve the productivity of the multi-core fiber made by the effective use of the existing fabrication technology and knowledge.

   • Sufficiently low span loss which is comparable to conventional SMF was achieved concatenating the standard diameter multi-core fibers fabricated by different vendors intentionally.

   Figure 3 Schematic image of multi-core transmission line composed of different vendors and its loss characteristics
3. Beyond 100 Tera-bit transmission

A multi-core transmission system was constructed by concatenating three spans. Three multi-core optical amplifiers fabricated by NEC, KDDI Research, NTT, and Furukawa were inserted at each end of three spans in order to compensate the signal attenuation. Cladding pumping type multi-core optical amplifiers which is expected to reduce power consumption were used, and a 16% improvement was confirmed in this achievement*8. In order to confirm the capability of the constructed multi-core transmission line to beyond 100

Tera-bit/s transmission, 16QAM*9 based 116-wavelength signals were prepared and the output signal quality after 316 km long transmission were examined.

Fan-In/Fan-Out devices*10 fabricated by NTT and Furukawa were used to input/output signals to/from each

core of multi-core fiber. Pluggable optical connectors*11 with existing MU-type or SC-type interfaces, fabricated by CIT and NTT, were used to connect the input/output end of the multi-core transmission lines and Fan-In/Fan-Out devices. These optical connectors have rotational alignment features in order to connect the facing four-cores correctly. Thus, the low loss and pluggable optical connection of multi-core structure was achieved.

Satisfactory well transmission quality was confirmed in all cores and all wavelengths, this result is the world's largest transmission capacity of 118.5 Tera-bit/s *12 among a standard diameter optical fiber. These achievements reveal that multi-core fiber with standard diameter can be used to realize an ultra large capacity transmission system overcoming the capacity crunch in the current SMF.